- Classifications
- EN ISO 14343-A : G 19 9 L Si
SFA/AWS A5.9 : ER308LSi
Werkstoffnummer : ~1.4316 - Approvals
- BV : 308L SA BT (M12)
CE : EN 13479
CWB : ER308LSi
DB : 43.039.01
DNV-GL : VL 308 L (M13)
NAKS/HAKC : 0.8-1.2 mm
UKCA : EN 13479
VdTÃœV : 04267 - Alloy Type
- Austenitic (with approx. 8 % ferrite) 19% Cr - 9% Ni - Low C - High Si
- Shielding Gas
- M12, M13 (EN ISO 14175)
- Packaging
- 1.0mm / 15kg
- Diameter (Ø)
- 1.0 mm
Suvirinimo viela OK Autrod 308LSi - OK Autrod 308LSi 1.0mm 15kg
1263046
Price
€210.16
VAT incl.
Stock Quantity:
Kaunas Shop
(1 pcs)
Central warehouse
not available
Delivery terms:
FREE pick up tomorrow, in the store, Raudondvario pl. 141, Kaunas
(€0.00)
We will deliver the product to you via: 1-2 w.d. Venipak
(€6.00)
We will deliver the product to you via: 1-2 w.d. Venipak pickup (paštomatas)
(€8.00)
Description
A continuous solid corrosion resisting chroumium-nickel wire for welding of austenitic chromium nickel alloys of 18% Cr - 8% Ni-type. OK Autrod 308LSi has a good general corrosion resistance. The alloy has a low carbon content which makes this alloy particularly recommended where there is a risk of intergranular corrosion. The higher silicon content improves the welding properties, such as wetting. The alloy is widely used in the chemical and food processing industries as well as for pipes, tubes and boilers.
Specifications
Approvals are based on factory location. Please contact ESAB for more information.
| Typical Tensile Properties | |||
|---|---|---|---|
| Condition | Yield Strength | Tensile Strength | Elongation |
| As Welded | 420 MPa | 570 MPa | 36 % |
| Tested at 350°C. | |||
| As Welded | 370 MPa | 490 MPa | |
| Typical Charpy V-Notch Properties | ||
|---|---|---|
| Condition | Testing Temperature | Impact Value |
| As Welded | 20 °C | 105 J |
| As Welded | -60 °C | 70 J |
| As Welded | -196 °C | 40 J |
| Typical Wire Composition % | |||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| C | Mn | Si | S | P | Ni | Cr | Mo | Cu | N | Nb | FN WRC-92 |
| 0.01 | 1.8 | 0.8 | 0.012 | 0.013 | 10.0 | 20.0 | 0.1 | 0.10 | 0.06 | 0.02 | 8 |
| Typical Weld Metal Analysis % | |||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| C | Mn | Si | S | P | Ni | Cr | Mo | Cu | N | Nb | FN WRC-92 |
| 0.03 | 1.8 | 0.7 | 0.009 | 0.020 | 10.0 | 19.5 | 0.03 | 0.1 | 0.04 | 0.01 | 6 |
| Deposition Data | ||||
|---|---|---|---|---|
| Diameter | Current | Voltage | Wire Feed Speed | Deposition Rate |
| 0.8 mm | 55-160 A | 15-24 V | 4.0-17.0 m/min | 1.0-4.1 kg/h |
| 0.9 mm | 65-220 A | 15-28 V | 3.5-18.0 m/min | 1.1-5.4 kg/h |
| 1.0 mm | 80-240 A | 15-28 V | 4.0-16.0 m/min | 1.5-6.0 kg/h |
| 1.2 mm | 100-300 A | 15-29 V | 3.0-14.0 m/min | 1.6-7.5 kg/h |
| 1.6 mm | 230-375 A | 23-29 V | 5.5-9.0 m/min | 5.2-8.6 kg/h |