Suvirinimo viela ESAB OK AristoRod 12.50 - 1.0mm / 18kg

Classifications: CSA W48 : B-G 49A 3 C1 S6
EN ISO 14341-A : G 38 3 C1 3Si1
EN ISO 14341-A : G 3Si1
EN ISO 14341-A : G 42 4 M20 3Si1
EN ISO 14341-A : G 42 4 M21 3Si1
JIS Z 3312 : YGW 12(C1)
SFA/AWS A5.18 : ER70S-6
Approvals: ABS : 3Y SA
BV : SA3YM
CE : EN 13479
CWB : B-G 49A 3 C1 S6
DB : 42.039.29
DNV-GL : III YMS
JIS : YGW12 (C1)
LR : 3YS H15
NAKS/HAKC : 1.0-1.6 mm
NAKS/HAKC : 1.2-1.6 mm
PRS : 3YS (C1, M21)
RINA : 3Y S
UKCA : EN 13479
VdTÜV : 10052
Alloy Type: Carbon-manganese steel (Mn/Si-alloyed)
Shielding Gas: M20, M21, C1 (EN ISO 14175)
Packaging: 1.0mm / 18kg
Diameter (Ø): 1.0 mm
AWS Classification: ER70S-6

Brand

Suvirinimo viela ESAB OK AristoRod 12.50 - 1.0mm / 18kg

Name: Suvirinimo viela ESAB OK AristoRod 12.50 - 1.0mm / 18kg
Brand: Esab
SKU: 1263754
Price: 73 EUR
Availability: InStock

Reference 1263754

Price €73.00 VAT incl.

‹

›

Stock Quantity:

Kaunas Shop
(1 pcs)

Central warehouse
not available

Delivery terms:

FREE pick up today, in the store, Raudondvario pl. 141, Kaunas (€0.00)

We will deliver the product to you via: 1-2 w.d. Venipak (€4.00)

Show all delivery methods

Description

The non copper coated OK AristoRod 12.50 is a manganese-silicon alloyed solid wire for GMAW of unalloyed steels, such as general structural, pressure vessel, ship building and for fine-grained carbon-manganese steels for the same purpose with a minimum yield strength of max 420 MPa. The electrode can be welded with either a gas mixture or with pure CO2 as the shielding gas. The AristoRod wires are suitable for operating at high currents with maintained disturbance free wire feeding giving a stable arc with a low amount of spatter. OK AristoRod 12.50 delivered in the unique Esab Octagonal Marathon Pac is excellent in mechanised welding applications.

Specifications

Approvals are based on factory location. Please contact ESAB for more information.

Typical Tensile Properties
Condition	Yield Strength	Tensile Strength	Elongation
AWS C1
As Welded	430 MPa	530 MPa	30 %
EN C1
As Welded	440 MPa	540 MPa	25 %
EN M21
As Welded	470 MPa	560 MPa	26 %
Stress Relieved 15 hour(s) 620 °C	370 MPa	495 MPa	28 %

Typical Charpy V-Notch Properties
Condition	Testing Temperature	Impact Value
AWS C1
As Welded	-30 °C	75 J
EN C1
As Welded	-30 °C	75 J
As Welded	20 °C	110 J
EN M21
Stress Relieved	-20 °C	90 J
Stress Relieved	20 °C	120 J
As Welded	-20 °C	120 J
As Welded	-40 °C	90 J
As Welded	-30 °C	100 J
As Welded	-50 °C	70 J
As Welded	20 °C	130 J

Typical Weld Metal Analysis %
C	Mn	Si	S	P	Cu	Ti+Zr
C1
-	-	-	-	-	-	<0,01
M21
-	-	-	-	-	-	<0,01
0.08	0.94	0.63	0.012	0.013	0,07	-

Typical Wire Composition %
C	Mn	Si
0.08	1.46	0.85

Deposition Data
Diameter	Current	Voltage	Wire Feed Speed	Deposition Rate
0.8 mm	60-200 A	18-24 V	3.2-10.0 m/min	0.8-2.3 kg/h
0.9 mm	70-250 A	18-26 V	3.0-12.0 m/min	0.9-3.5 kg/h
1.0 mm	80-300 A	18-32 V	2.7-15.0 m/min	1.0-5.5 kg/h
1.14 mm	100-350 A	18-34 V	2.6-15.0 m/min	1.2-7.0 kg/h
1.2 mm	120-380 A	18-35 V	2.5-15.0 m/min	1.3-8.0 kg/h
1.32 mm	130-400 A	19-35 V	2.4-15.0 m/min	1.5-8.5 kg/h
1.4 mm	150-420 A	22-36 V	2.3-12.0 m/min	1.6-8.7 kg/h
1.6 mm	225-550 A	28-38 V	2.3-10.0 m/min	2.1-9.4 kg/h
2.0 mm	300-650 A	32-44 V	3.0-7.0 m/min	4.4-10.2 kg/h